Polyol and Isocynate Resin For shoe sole

Polyol and Isocynate Resin For shoe sole
Product Detailed
sports shoe,lady shoe,slippers 1.good handle,low density and shine bright surface 2. Hardness from 40shoreA -- 70A

Characteristic: Good handle, smooth surface,

                         low density and good dimension stability

Application:Sole ,slippers,lady shoes

Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPa·s/40°C)

Density (g·cm-3/40°C)

Package(kg)

A-2260

Liquid

800~1200

1.01~1.02

225

B-8580

Yellowish transparent liquid or waxy

600~800

1.08~1.2

225

 Materials preheat

A-2260:      preheated at 50~60°C for16~18 hours          

B-8580:      preheated at 50~60°C for 18~20 hours

Typical processing parameters & Reaction parameter

Items

A/B Materials Temperatures(°C)

A+C/B Mix ratio(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature(°C)

Demold Time(min)

Parameter

40~45/38~42

100/96~98

6~8

40~50

0.15~0.25

45~55

4~5

 The adding content of C-2 should be 270g±20g/18kg

      The adding content of water should be 0~100g/18kg according to the reality

         The adding content of hardener should be changed according to the reality

Physical properties 

Items

Molded Density (g/cm3)

Hardness

(Shore A )

Tensile strength

(MPa)

Elongation (%)

Tear Strength

(kN/m)

Flexing resistance

  Break length 4mm

(20°C)

Physical  properties

0.30~0.45

45~70

4.0~6.0

250~400

18~26

No crack

Demold time may be prolonged with the increase of sole thickness

These physical data are acquired by testing a sample of 6mm thick.

Data listed above are just for reference. The detail data are subjected to practical production. If other requests for Physical properties, please contact us.

We are the leading manfucature of Pu resins for shoe sole:

We can use this grade material to make beautiful slippers and sports shoes.