Typical properties of PU matrix
Name of product | Apperance | Viscosity(mPa·/40°C) | Density(g·cm/40°C) | Package(kg) |
A-3070 | liquid | 1000-1400 | 1.01-1.02 | 18 |
B-8280 | Yellowish Transparent Liquid or Waxy | 800-1200 | 1.08-1.2 | 20 |
Material preheat
A-3070 Preheated at 50-60°C for 6-8 hours
B-8280 Preheated at 60-70°C for 8-12 hours
Typical processing parameters & Reaction parameter
Items | A/B Materials Temperature(°C) | A+C/B Mix ratio (by weight) | Cream Time(s) | End of rise time(s) | Free rise foam density(g/cm³) | Mold temperature (°C) | Demold time(min) |
Parameter | 40-45/38-42 | 100/101-103 | 8-10 | 60-70 | 0.24-0.26 | 45-55 | 5-7 |
The adding content of C-2 should be 250g±20/18kg
The adding content of water should be 0-90g/18kg according to the reality
The adding content of hardener should be changed according to the reality
Physical properties
Items | Molded Density(g/cm³) | Hardness(shore A) | Tensile strength(Mpa) | Elongation(%) | Tear Strength(kN/m) |
Physical properties | 0.50-0.70 | 55-68 | 7.5-9.0 | 340-450 | 24-33 |
Demold time may be prolonged with the increase of sole thickness.
These physical date are acquired by testing a sample of 6mm thick.
Data listed above are just for reference, The detail date are subjected to practical production, If other request for Physical properties, please contact us.
polyester tire